上海热处理网＞＞热处理行业的网上平台＞＞新闻动态 - 渗碳或碳氮共渗件磨削裂纹的控制 关键词 ：渗碳；磨削裂纹；涂料 [gap=664]Key Words: carburizing; grinding crack; paint
基于14个网页-相关网页
The results show the surface circular defect was grinding crack which mainly caused by the inappropriate grinding technology. And insufficient tempering after quenching contributed to the initiation of the grinding cracks.
结果表明:表面的环状缺陷为磨削裂纹,磨削工艺不当是造成磨削裂纹的主要原因,同时淬火后回火不充分进一步加剧了磨削裂纹的产生。
参考来源 - 电机轴表面缺陷分析·2,447,543篇论文数据，部分数据来源于NoteExpress
The article explains the causation of grinding crack, affecting factor and controlling steps.
介绍了产生磨削裂纹的原因、影响因素及控制措施。
The cause of the grinding crack on medium frequency induction hardened CAM shaft made of spheroidal cast iron was analyzed.
对球墨铸铁中频淬火凸轮轴磨削裂纹产生的原因进行了分析。
According to the mechanism that micro-cracks come into being from the dislocation, the dislocation piled-up model is used to describe the grinding crack.
研究中，将宏观断裂力学及微观断裂物理相结合，根据位错产生微裂纹机制，对磨削过程的微裂纹的形成采用位错赛积模型来描述。